Name: 5mm Dia., 0.5mm Thick, 400-1100nm, High Durability AR Coated Sapphire Window
SKU: 18-461
Price: RMB 903.44

5mm Dia., 0.5mm Thick, 400-1100nm, High Durability AR Coated Sapphire Window

High Durability Anti-Reflection (AR) Coated Sapphire Windows

产品编码 #18-461 6-10 工作日

- +

RMB 587.24 ~~RMB 903.44~~

数量 1-10
RMB 587.24 ~~RMB 903.44~~

数量 11+
RMB 529.95 ~~RMB 815.30~~

含税批量价格
索取报价

+ 添加至收藏夹
Create an account or log in to access saved list

产品对比

下载产品资料

色散系数 (v_d):

72.24

轴方向:

Random

倒角:

Protective as needed

双折射率 (n_o-n_e) :

0.008 for Visible Light Orthogonal to Optical Axis

有效孔径 (%):

有效孔径 CA（mm）:

4.50

直径 (mm):

5.00 ±0.05

厚度 (mm):

0.50 ±0.05

涂层:

Hardened VIS-NIR (400-1100nm)

涂层规格:

R_avg <1.5% @ 400 - 1100nm
R_abs <2.0% @ 400 - 1100nm

热膨胀系数 CTE (10^-6/°C):

8.8

密度 (g/cm³):

3.97

边缘:

Fine Ground

折射率 n_d:

1.77

努氏硬度 (kg/mm²) :

1900

平行度（弧分）:

≤3.5

泊松比 :

0.27

基底: Many glass manufacturers offer the same material characteristics under different trade names. Learn More

Sapphire (Al₂O₃)

表面平整度 (P-V):

2λ (typical)

表面质量:

80-50

类型:

Protective Window

波长范围 (nm):

400 - 1100

杨氏模量 (GPa) :

435

Coating Abrasion:

Severe, per MIL-C-675C Paragraph 4.5.10

Coating Adhesion:

Per MIL-M-13508C Paragraph 4.4.6

Coating Humidity:

≥24 Hours per MIL-C-675C paragraph 4.5.8

Coating Salt Solubility:

≥24 Hours Immersion per MIL-C-675C paragraph 4.5.7

Coating Salt Spray:

≥24 Hours per MIL-C-675C paragraph 4.5.9

Coating Temperature (°F):

-80 to +160 per MIL-M-13508C Paragraph 4.4.4

合规性

RoHS:

符合标准

Certificate of Conformance:

浏览

产品系列说明

达到 MIL-C-675C 的严重磨损要求
400-1100nm 或 2000-5000nm 的低反射镀膜
适用于需要薄型光学元件的恶劣环境
另有未镀膜蓝宝石窗口片可供选择

高耐用性增透镀膜蓝宝石窗口片是为需要蓝宝石坚固性的应用而设计的，增透镀膜设计可承受严重磨损。这些蓝宝石窗口片上的增透镀膜被设计为能够承受从-80到+160°F的温度循环、连续24小时的盐雾、以及24小时的盐溶浸泡。镀膜设计可满足 MIL-C-675C 对可见-近红外和中波红外应用的严重磨损要求，非常适合在恶劣环境中使用。高耐用性增透镀膜蓝宝石窗口片用于航空航天、国防和工业应用，以及任何需要厚度薄且耐用的保护窗口片的光学应用。